Low temperature cross-linked POF shrink at 100 centigrade and shrinkage can achieve around 30%. At 120 centigrade, the shrinkage will achieve 78%. It features lower shrink temperature, faster shrink speed, firmer seal and softer and smaller "dog ear". Low-Temperature Cross-Linked POF shrink film is designed to reduce the amount of heat exposure required to shrink the film. It is perfect for heat-sensitive items like chocolates, candies, baked goods, and electric component, cosmetic, toy, etc as well. Moreover, it is able to be compatible with all kinds of machines. Additionally, due to lower temperatures, the packaging machine components like blades, and hot knives last longer, which also reduce cost in long term.
Low-Temperature Cross-Linked POF Shrink Film
Low-Temperature Cross-Linked POF Shrink Film
Properties:
| |||||||||||||||
TEST ITEM | UNIT | ASTM TEST | TYPICAL VALUE | ||||||||||||
THICKNESS | 12um | 15um | 19um | 25um | 38um | ||||||||||
OPTICAL | |||||||||||||||
HAZE | % | D1003 | 2.4 | 2.5 | 2.8 | 3.1 | 4.0 | ||||||||
CLARITY | % | D1746 | 99 | 98.8 | 98 | 94 | 91.5 | ||||||||
% | D2457 | 88.5 | 88 | 87.5 | 86 | 85 | |||||||||
SHRINKAGE PROPERTIES | MD | TD | MD | TD | MD | TD | MD | TD | MD | TD | |||||
FREE SHRINKAGE | @100℃ | % | D2732 | 30 | 31 | 29 | 30 | 29 | 31 | 29 | 30 | 29 | 31 | ||
@120℃ | 76 | 77 | 77 | 78 | 75 | 77 | 75 | 76 | 77 | 76 | |||||
TENSILE | |||||||||||||||
TENSILE STRENGTH(MD) | N/mm2 | D882 | 110 | 110 | 115 | 115 | 115 | ||||||||
TENSILE STRENGTH(TD) | 110 | 110 | 115 | 115 | 115 | ||||||||||
ELONGATION(MD) | % | 120 | 120 | 125 | 125 | 125 | |||||||||
ELONGATION(TD) | 120 | 120 | 125 | 125 | 125 | ||||||||||
TEAR STRENGTH | |||||||||||||||
MD | g | D1922 | 11.5 | 14.8 | 19.0 | 25.0 | 33.3 | ||||||||
TD | 11.9 | 15.3 | 20.0 | 26.2 | 32.9 | ||||||||||
SEAL STRENGTH | |||||||||||||||
HOT WIRE SEAL(MD) | N/mm | F88 | 1.12 | 1.5 | 1.8 | 2.3 | 3 | ||||||||
HOT WIRE SEAL(TD) | 1.05 | 1.15 | 1.6 | 2.2 | 2.9 | ||||||||||
COF (FILM TO FILM) | |||||||||||||||
DYNAMIC | μd | D1894 | 0.22 | 0.23 | 0.22 | 0.22 | 0.23 |
NOTE: These values are typical data for Sunward POF shrink film and are not intended as use for limiting specifications.
Our products have gained reputation domestically and globally. The rigid qualtiy control procedures are implemented throught every step in the production process from raw material sourcing and package. We seek to build up cooperation relationship with customers for more properous future. If you are interested in any of our products, please contatct us freely!
Low temperature cross-linked POF shrink at 100 centigrade and shrinkage can achieve around 30%. At 120 centigrade, the shrinkage will achieve 78%. It features lower shrink temperature, faster shrink speed, firmer seal and softer and smaller "dog ear". Low-Temperature Cross-Linked POF shrink film is designed to reduce the amount of heat exposure required to shrink the film. It is perfect for heat-sensitive items like chocolates, candies, baked goods, and electric component, cosmetic, toy, etc as well. Moreover, it is able to be compatible with all kinds of machines. Additionally, due to lower temperatures, the packaging machine components like blades, and hot knives last longer, which also reduce cost in long term.
Low-Temperature Cross-Linked POF Shrink Film
Low-Temperature Cross-Linked POF Shrink Film
Properties:
| |||||||||||||||
TEST ITEM | UNIT | ASTM TEST | TYPICAL VALUE | ||||||||||||
THICKNESS | 12um | 15um | 19um | 25um | 38um | ||||||||||
OPTICAL | |||||||||||||||
HAZE | % | D1003 | 2.4 | 2.5 | 2.8 | 3.1 | 4.0 | ||||||||
CLARITY | % | D1746 | 99 | 98.8 | 98 | 94 | 91.5 | ||||||||
% | D2457 | 88.5 | 88 | 87.5 | 86 | 85 | |||||||||
SHRINKAGE PROPERTIES | MD | TD | MD | TD | MD | TD | MD | TD | MD | TD | |||||
FREE SHRINKAGE | @100℃ | % | D2732 | 30 | 31 | 29 | 30 | 29 | 31 | 29 | 30 | 29 | 31 | ||
@120℃ | 76 | 77 | 77 | 78 | 75 | 77 | 75 | 76 | 77 | 76 | |||||
TENSILE | |||||||||||||||
TENSILE STRENGTH(MD) | N/mm2 | D882 | 110 | 110 | 115 | 115 | 115 | ||||||||
TENSILE STRENGTH(TD) | 110 | 110 | 115 | 115 | 115 | ||||||||||
ELONGATION(MD) | % | 120 | 120 | 125 | 125 | 125 | |||||||||
ELONGATION(TD) | 120 | 120 | 125 | 125 | 125 | ||||||||||
TEAR STRENGTH | |||||||||||||||
MD | g | D1922 | 11.5 | 14.8 | 19.0 | 25.0 | 33.3 | ||||||||
TD | 11.9 | 15.3 | 20.0 | 26.2 | 32.9 | ||||||||||
SEAL STRENGTH | |||||||||||||||
HOT WIRE SEAL(MD) | N/mm | F88 | 1.12 | 1.5 | 1.8 | 2.3 | 3 | ||||||||
HOT WIRE SEAL(TD) | 1.05 | 1.15 | 1.6 | 2.2 | 2.9 | ||||||||||
COF (FILM TO FILM) | |||||||||||||||
DYNAMIC | μd | D1894 | 0.22 | 0.23 | 0.22 | 0.22 | 0.23 |
NOTE: These values are typical data for Sunward POF shrink film and are not intended as use for limiting specifications.
Our products have gained reputation domestically and globally. The rigid qualtiy control procedures are implemented throught every step in the production process from raw material sourcing and package. We seek to build up cooperation relationship with customers for more properous future. If you are interested in any of our products, please contatct us freely!